Everit, electrolytic nickel-plating

Everisation is a method for electrolytic Nickel-plating for iron and various steel qualities where the coating is a cold process with bath temperatures less than 40 oC.

The process gives a completely homogenous connection to the base material without any intermediate plating and where heat tension cannot occur. It is an excellent alternative to Inconell welding.

Everised parts can be machined the same way as the base material and the parts can be forged, bent in hot or cold condition, turned, ground or milled without causing the coating to delaminate.

The Everit coating is applied from 0.01 to more than 3 millimetres on parts of
wrought iron, steel, stainless steel, cast steel, alloyed structural steel as well as rolled and cast metal.

The properties and areas of utilisation are well documented, and over the years a number of tests have been carried out. Copies of the test reports can be conveyed on application.

Properties of the Everit coating:


Hardness, normal coating
240 - 280 HV

Hardness, top coating
500 - 550 HV

Tensile strength
650 - 700 N/mm2

Elongation, normal coating
20 - 17 %

Elongation, top coating
0,5 - 0,2%

Adhesion to steel
400 - 500 N/mm2

Coefficient of thermal expansion
13* 10-6

Thickness, normal coating
0,01 - > 3,00 mm

Thickness, top coating
0,01 - 0,2 mm